Stanley 633Used where ultimate machinability is a factor. Also ideal for repairing very thin or eroded sections of cast iron.
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
"Pulsed Arc" high nickel, shallow penetration cast iron minimizes heat affected zone hardening
• "Low temperature" gentle globular arc transfer.
• Excellent arc control in all positions.
• Weld deposits are extremely soft and machinable due to minimal dilution.
• Also available in TIG as product code STANLEY 633 TIG. |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
TYPICAL MECHANICAL PROPERTIES :
Undiluted Weld Metal Maximum Value Up to:
Tensile strength 62,000 Psi ( 440 MPa )
Yield strength 44,000 Psi ( 300 MPa )
Elongation 30 %
Hardness Rockwell B80-82, Brinell 150
APPLICATIONS :
Used where ultimate machinability is a factor. Also ideal for repairing very thin or eroded sections of cast iron.
MICROSTRUCTURE :
Austenitic nickel with finely distributed graphite flakes.
RECOMMENDED CURRENT :
DC Straight (-) or AC
RECOMMENDED AMPERAGE SETTINGS :
Diameter (mm) 3/32 (2,5) 1/8 (3,2) 5/32 (4,0)
Minimum Amperage 50 70 100
Maximum Amperage 70 100 130
WELDING POSITIONS :
Flat, Vertical up, Vertical down, Horizontal, Overhead.
WELDING TECHNIQUES :
The arc gap should be as short as feasible. Move in direction of travel according to the rate of alloy flow.
|
|