Stanley 129Unique alloy for repair & built-up of all Air hardening tool steels.
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Unique alloy for repair & build-up of all Air Hardening tool steels.
- Deposits are highly crack resistant, forgeable and temperable.
- High alloy deposits are very tough and will endure extreme impact and abrasion conditions.
- Operates in all positions.
- Also available in TIG form as item
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
APPLICATIONS:
Ideal for repairing and rebuilding shear blades, percussion drills, earth borers, crusher jaws, etc.
MICROSTRUCTURE:
Tempered Martensite
FLUX COLOR: Grey
TYPICAL MECHANICAL PROPERTIES:
Undiluted Weld Metal
Hardness
|
Maximum Value Up to:
Rockwell C55-60 |
RECOMMENDED CURRENT: AC, DC + or -
RECOMMENDED AMPERAGE SETTINGS:
| Diameter (mm) |
3/32 (2.5) |
1/8(3.25) |
5/32 (4.0) |
3/16(5.0) |
| Minimum Amperage |
45 |
80 |
130 |
150 |
| Maximum Amperage |
90 |
120 |
160 |
175 |
WELDING POSITIONS: Flat, Horizontal, Vertical up
DEPOSITION RATES:
Diameter
(mm) |
Length
(mm) |
Weldmetal/
Electrode |
Electrodes per lb
(kg) of Weldmetal |
Arc Time of
Deposition
min/lb (kg) |
Amperage
Setting |
Recovery
Rate |
| 3/32(2.5) |
14" (350) |
.94oz(26g) |
17(37) |
22(49) |
80 |
120% |
| 1/8 (3.25) |
14" (350) |
.94oz(26g) |
17(37) |
22(49) |
115 |
120% |
| 5/32 (4.0) |
14" (350) |
1.8oz(50g) |
9(19) |
16(35) |
150 |
120% |
| 3/16 (5.0) |
14" (350) |
2.7oz(75g) |
6(14) |
11(25) |
170 |
120% |
WELDING TECHNIQUES:
Do not pre-heat. Use string or weave bead technique to deposit material. Avoid overheating on any manganese steel base metals.
ELECTRODE PACKAGING & DIMENSIONS:
| Diameter(mm) |
3/32(2.5) |
1/8 (3.25) |
5/32 (4.0) |
3/16(5.0) |
| Length (mm) |
14"(350) |
14"(350) |
14"(350) |
14" (350) |
| Electrodes / lb |
20 |
13 |
9 |
6 |
| Electrodes / kg |
44 |
28 |
20 |
13 |
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
|
|
|
|
|