Stanley 606Economy hardfacing electrode for abrasion and moderate impact.
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Economical hardfacing electrode for abrasion and moderate impact
- The best hardfacing electrode for low open circuit voltage AC welding machines.
- Spray transfer allows for smooth, uniform overlays.
- Hardness of RC 56-58 allows for good abrasion resistance along with moderate impact resistance.
- Also available as a special tubular wire as Product code Stanley 606 MIG
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
APPLICATIONS:
General hardfacing where some impact is combined with abrasion.
MICROSTRUCTURE:
In the as-deposited condition, the microstructure consists of martensite and some carbides.
FLUX COLOR: Grey
TYPICAL MECHANICAL PROPERTIES:
Undiluted Weld Metal
H a r d n e s s
Wear Co-efficient |
Maximum Value Up to:
Rockwell C56-58
2.8% |
RECOMMENDED CURRENT: DC Reverse (+) or AC
RECOMMENDED AMPERAGE SETTINGS:
| Diameter (mm) |
1/4(6.5) |
5/32 (4.0) |
3/16 (5.0) |
| Minimum Amperage |
100 |
150 |
200 |
| Maximum Amperage |
130 |
190 |
260 |
WELDING POSITIONS: Flat, Horizontal
DEPOSITION RATES:
Diameter
(mm) |
Length
(mm) |
Weldmetal/
Electrode |
Electrodes per lb
(kg) of Weldmetal |
Arc Time of
Deposition
min/lb (kg) |
Amperage
Setting |
Recovery
Rate |
| 1/4 (6.5) |
14" (350) |
.9oz (26g) |
18 (39) |
23 (50) |
110 |
130% |
| 3/8 (9.75)) |
14" (350) |
2.5oz (71g) |
6 (14) |
17 (37) |
165 |
130% |
| 1/2 (13.0) |
14" (350) |
3.7oz (105g) |
4 (9) |
13 (29) |
230 |
130% |
WELDING TECHNIQUES:
Weld deposits are best applied using a weave technique. Full undiluted hardness is usually achieved after 2 to 3 passes.
ELECTRODE PACKAGING & DIMENSIONS:
| Diameter(mm) |
1/8 (3.25) |
5/32 (4.0) |
3/16 (5.0) |
| Length (mm) |
14" (350) |
14" (350) |
14" (350) |
| Electrodes / lb |
12 |
8 |
6 |
| Electrodes / kg |
26 |
18 |
13 |
|
|
Overview |
|