Stanley 20 / 20F / 20RibbonHigh Strength Self Fluxing 15% Silver Torch Alloy for Copper to Copper
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
High strenght, hight silver, self-fluxing torch alloy for copper to copper and coper to brass.
For smooth ductile deposits that wil not leak and will withstand severe vibration. Silver content provides thin flowing properties and low application temperature which preventa scaling on inside of tubing and minimizes annealing of copper. provides exellent corrosion resistance and can be spplied to dirty copper if necessary. leaves no flux residue on copper to copper joints and has 98% to 99% conductivity on pure copper. excellent capillary action. |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Applications :
- Electrical wiring
- Air condituonong and refrigeration
- Motors, brewery coils, armatures and electrical contacts.
- Bus bars, instruments, plumbing, brass or copper fittings.
How to Use :
Clean joint area. when joining copper to copper, can be applied wothout flux. Use a large size tip, carburizing flame and heat area broadly. Keep flame 2" to 3" from base metal and keep torch in constant motion.
When joining brass or bronze to copper or brass to bronze, use 20 flux. Paint paste along joint line and heat broadly until, keeping torch in constant motion. When a continuous fillet is observed, remove flame and allow molten metal to solidify. Flux residues should be removed by washing in warm water.
Typical Properties :
- Temperature : 1300 F (710 C)
- Tensile strength : 60,000 PSI
- Sizes : 1/16", 3/23", 1/8"
|
|